OK Autrod 316L

ESAB

OK Autrod 316L

The following items have been added to your list


x

A continous solid corrosion resisting chromium-nickel-molybdenum wire for welding of austenitic stainless alloys of 18% Cr - 8% Ni and 18% Cr - 10% Ni - 3% Mo-types. OK Autrod 316L has a good general corrosion resistance, particularly against corrosion in acid and chlorinated environments. The alloy has a low carbon content which makes it particularly recommended were there is a risk of intergranular corrosion. The alloy is widely used in the chemical and food processing industries as well as in ship building and various types of architectural structures.

BUY NOW


Typical Charpy V-Notch Properties

Impact Value Testing Temperature
as welded
55 J (40.5 ft-lb) -196 degC (-321 degF)
95 J (70 ft-lb) -60 degC (-76 degF)
120 J (88.5 ft-lb) 20 degC (68 degF)
sht 1050°c (1922°f) 0.5h
50 J (67 ft-lb) -196 degC (-321 degF)
90 J (66 ft-lb) -60 degC (-76 degF)
110 J (81 ft-lb) 20 degC (68 degF)

Typical Tensile Properties

Condition As Welded As Welded SHT SHT
1050°C 0.5h 1050°C 0.5h
Shielding Gas Tested at 350°C. Tested at 350°C.
Tensile Strength 440 MPa 620 MPa 590 MPa 430 MPa
Yield Strength 340 MPa 440 MPa 350 MPa 250 MPa
Elongation 26 % 37 % 42 % 31 %

Deposition Data

Current Deposition Rate Diameter Voltage Wire Feed Speed
55-160 A 1.0-4.1 kg/h (2-9 lb/h) 0.8 mm (0.030 in.) 15-24 V 4.0-17.0 m/min (157-669 in./min)
80-240 A 1.5-6.0 kg/h (3-13 lb/h) 1.0 mm (0.040 in.) 15-28 V 4.0-16.0 m/min (157-630 in./min)
100-300 A 1.6-7.5 kg/h (3-16 lb/h) 1.2 mm (0.047 in.) 15-29 V 3.0-14.0 m/min (118-551 in./min)
230-375 A 5.2-8.6 kg/h (11-19 lb/h) 1.6 mm (1/16 in.) 23-31 V 5.5-9.0 m/min (217-354 in./min)
80-240 A 1.5-6.0 kg/h (3-13 lb/h) 1.14 mm (0.045 in.) 15-28 V 4.0-16.0 m/min (157-630 in./min)
55-160 A 1.0-4.1 kg/h (2-9 lb/h) 0.9 mm (0.035 in.) 15-24 V 4.0-17.0 m/min (157-669 in./min)

Classifications

Wire Electrode Werkstoffnummer : ~1.4430
EN ISO 14343-A : G 19 12 3 L
SFA/AWS A5.9 : ER316L

Consumable Characteristics

Alloy Type Austenitic (with appr. 8 % ferrite) 19 % Cr - 12 % Ni - 3 % Mo - Low C

Typical Weld Metal Analysis %

Typical Wire Composition %
C Cr Cu FN WRC-92 Mn Mo N Ni P S Si
0.01 % 18.2 % - 7 % 1.7 % 2.6 % 0.04 % 12.0 % - - 0.4 %
Typical Weld Metal Analysis %
0.02 % 18.5 % 0.1 % - 1.8 % 2.7 % - 12 % 0.015 % 0.015 % 0.4 %
x

Part Numbers and Accessories

Select All | Select None

Check box to add

Part Numbers : OK Autrod 316L
1630169820 FIND A DISTRIBUTOR
1630084600 FIND A DISTRIBUTOR
1630099820 FIND A DISTRIBUTOR
1630109820 FIND A DISTRIBUTOR
1630129820 FIND A DISTRIBUTOR
1630129320 FIND A DISTRIBUTOR
163012342W FIND A DISTRIBUTOR
163016982A FIND A DISTRIBUTOR
163016342W FIND A DISTRIBUTOR

ESAB EQUIPMENT WARRANTIES ARE VALID ONLY WHEN PURCHASED THROUGH AN ESAB AUTHORIZED DEALERSHIP.

x
x

x

Loading..